Semiconductor Manufacturing |

Semiconductor Manufacturing

Semiconductor Manufacturing

Humidity/Moisture causes corrosion of ‘Circuit Points’, condensation on microchips circuit surface and improper adhesion of photo resists causing operational failure of Semiconductor Assembly.

General Recommendations

Relative Humidity in Semiconductor Assembly Manufacturing Areas should be maintained at 30% RH at 20°C (70°F).

Our Solutions

Semiconductors… microcircuits and microchips – manufacturing requires very precise condition to be maintained in the manufacturing / processing area. Components used in assembly/processing of semiconductors are generally hygroscopic and thus highlysusceptible to high humidity conditions. A high Humidity condition causes operational failure of chips, improper adhesion, corrosion in circuit points and many other problems.

Image Gallery


Humidity Control…. An important variable to –

  • Prevent corrosion of ‘Circuit Points’.
  • Prevent condensation on microchips circuit surface.
  • Protect equipment
  • Better adhesion of photoresists

Thus, Humidity Control Becomes A Must In

1. Assembly Area

In the production of semiconductors and integrated circuits excessive moisture adversely effects the bonding process and increases defects. Photosensitive polymer compounds called photoresists are used to mask circuit lines for etching process. Due to their hygroscopic nature they absorb moisture resulting in the microscopic circuit lines being cut or bridged, leading to circuit failure.

2. Wafer Fabrication Area

During wafer manufacture the spinners spray developer on the wafer surface, causing the solvent present on the wafer to evaporate rapidly, thereby cooling the wafer surface. This results in condensation of water vapour from the air on the wafer surface. This extra water on the wafer causes characteristics of the developer to change. The resist also absorbs the moisture causing the polymer to swell. Controlling relative humidity at 30% eliminates the possibility of the cooling the wafer surface lower than the dewpoint of the air surrounding the wafer surface, thus preventing failure and spoilage.

3. Photo Lithography Room

Conditions in photolithography room need to maintained between 20% to 35% RH at about 70°F. Excessive moisture causes the silica to absorb moisture, resulting in improper adhesion of photoresist leading to stressfracture and surface defects.

4. Faster Vacuum Pump Down

If humidity levels are high, operation of vacuum equipments like cryopump is slowed down due to large load of water vapour. If the RH levels can be maintained around 30- 35% than the reduced considerably resulting in increased batch processing speed.

5. For Protection of EPI equipment

Water vapour or moisture condenses on chilled surfaces of epitaxial equipment corroding of components resulting in operation failure and slow down of the process. Bry-Air Desiccant Dehumidifiers can effectively maintain the most stringent humidity conditions required for semiconductor manufacturing areas, since they are capable of maintaining RH as low as 1% or even lower at a constant level, regardless of ambient conditions.